Description

The Pro Master multilayer Zirconia YUCERA embodies the highest level of requirements in mechanical performance, aesthetic consistency, and long-term reliability.
Developed for laboratories seeking a no-compromise solution, it combines an advanced multilayer architecture with 100 % TOSOH raw material, a global reference in dental zirconia powder.

With its 8 layers of natural gradients, the Pro Master offers a gradual and perfectly controlled transition between strength and translucency. Flexural strength ranges from 800 to 1300 MPa, while translucency varies from 43 % to 57 %, allowing precise replication of the tooth’s natural behavior from the incisal edge to the cervical area.

This intelligent design ensures a high-level aesthetic result, optimal occlusal comfort, and maximum clinical durability, including for complex restorations and long-span bridges.

Incisal Zone
High translucency combined with controlled strength provides a natural enamel-like appearance while minimizing wear on opposing teeth.

Intermediate Zone
Optical and mechanical properties change progressively and continuously, ensuring a natural, smooth, and perfectly integrated transition.

Cervical Zone
Increased hardness and strength at the cervical area ensure excellent structural stability, reducing the risk of chipping or cracking, while effectively masking underlying shades.

Zirconia Type : 4D Multilayer – 100% TOSOH Powder - 3Y/4Y/5Y

Translucency : 43-57 %

Flexural strength : 800 - 1300 MPa

Fracture strength : 5 MPa·Vm

Vickers hardness (HV10) : 1200

Density : ≥ 6.08 g ± 0.03 g/cm³

Recommended sintering temperature : 1500 °C

Application area

Single-unit full zirconia / Full zirconia bridge / Veneers / Layering

Available shades

A1 / A2 / A3 / A3.5 / A4 / B1 / B2 / B3 / B4 / C1 / C2 / C3 / C4 / D2 / D3 / D4 / BL1 / BL2 / BL3 / BL4

Availability

98.5mm : Permanent

95mm : Made to order